High-strength graphene and polyacrylonitrile composite fiber enhanced by surface coating with polydopamine
2019-11-13 16:55:36 조회수190
Hyunsoo Kim(a), Rouhollah Jalili(b), Geoffrey M.Spinks(c), Gordon G.Wallace(c), Seon Jeong Kim(a) a)Center for Self-Powered Actuation, Department of Biomedical Engineering, Hanyang University, Seoul 04763, Republic of Korea b)School of Science, College of Science, Engineering and Health, RMIT University, Melbourne, VIC 3001, Australia c)Intelligent Polymer Research Institute, ARC Centre of Excellence for Electromaterials Science, AIIM Facility, Innovation Campus, University of Wollongong, North Wollongong, NSW 2522, Australia 원문 링크 : https://www.sciencedirect.com/science/article/pii/S0266353816313331?via%3Dihub

Abstract

Carbon fibers are well-known reinforcing elements in advanced composites, but these materials remain expensive partly due to the complex processing methods used to form high strength and high modulus fibers. Graphene is seen as an alternative precursor for the formation of high strength carbon-based fibers. Here it is shown that the strength and modulus of graphene-based fibers are enhanced by incorporating a polyacrylonitrile (PAN) binder, surface coating with polydopamine (PDA) and through appropriate pyrolysis heat treatments. Fiber samples were prepared by a wet-spinning method such that the composition of liquid-crystalline graphene oxide (LCGO) and PAN could be varied over the full range. The maximum fiber mechanical strength (220 MPa) and modulus (19 GPa) occurred at a composition of LCGO (80 wt%) and PAN (20 wt%). The mechanical strength was further significantly increased to 526 MPa through pyrolysis of the LCGO/PAN fiber at 800 °C in a nitrogen atmosphere which caused carbonization of PAN. In addition, surface treatment of the LCGO/PAN fiber with PDA before carbonization improved the mechanical strength by an additional 40%. 

 
사이트맵 닫기